標題: 釔鋇銅氧高溫超導薄膜製作及其紅外線偵測之研究
Preparation of YBaCuO Superconducting Film and their Reasearch for Infrared Detection
作者: 王邁為
Mai-Wei Wang
曾俊元
Tseung-Yueng Tseng
電子研究所
關鍵字: 超導體 ;紅外線; 脈衝; 雜訊功率;superconductor; infrared;pulse;noise equivalent power
公開日期: 1992
摘要: 以直流濺射鍍膜系統,在氧化鎂基板上成長的釔鋇銅氧薄膜,經適當的退火 處理可擁有c軸方向及臨界溫度達84K的平坦薄膜o 這些成長所得之薄膜, 以光製版術及EDTA化學溶液蝕刻成兩種微橋, 再經0.94微米之紅外線脈衝 照射以研究熱輻射現象o在脈衝頻率2Hz的控制下,可得每單位入射功率354 伏特之響應o雜訊功率可估計為7.2 e -10 W/Hz0.5 o 在此實驗過程, 為 得到較佳的反應基板材料的選擇, 薄膜的品質, 電阻係數, 熱導, 偵測器 的形狀, 都必須給予適當的考量o Thin films of YBaCuO (Y-123) have been made by dc magnetron sputtering deposition on (100) Mgo substrates. THe experimental results show that the films, with flatness oriented in c-axis and a zero resistance temperature of 84K have been fabricated by an in-situ growth technique. A GaAs light emission diode with an 0.94 um wavelength was used as the light source to study the bolometric effect. Two types of bolometers (microbridge and meander) were made by photolithography with ethylenediametetra acetic acid (EDTA) as the wet etching solution. Measurement of the meander device on Mgo substrate yielded the bolometric responsivity of approximately 354.7 V/W , by illuminating a 2 Hz signal with 0.362 mW power. The noise equivalent power of this device have been estimated as 7.2 e -10 W/Hz0.5. Therefore, the detectivity is 1.04 e 9 cm Hz0.5/W. In this experiment several parameters, such as bias current, materials thermal coefficient of resistance and thermal conductance, were considered for the purpose of obtaining the best bolometric response.
URI: http://140.113.39.130/cdrfb3/record/nctu/#NT810430055
http://hdl.handle.net/11536/56917
Appears in Collections:Thesis