標題: Relationship between Microstructures and Tensile Properties of an Fe-30Mn-8.5Al-2.0C Alloy
作者: Lin, Chih Lung
Chao, Chuen Guang
Bor, Hui Yum
Liu, Tzeng Feng
材料科學與工程學系
Department of Materials Science and Engineering
關鍵字: iron-manganese-aluminum-carbon alloy;spinodal decomposition;tensile test;lamellar structure;ductility
公開日期: 1-六月-2010
摘要: Owing to the presence of a large amount of fine (Fe,Mn)(3)AlC carbides within austenite (gamma) matrix, the tensile property of the Fe-30%Mn-85Al%-20%C (in mass%) alloy in the as-quenched condition was clearly superior to that of the as-quenched FeMnAlC (C <= 1 3%) alloys investigated by previous workers After being aged at 823 K for 3 h, the present alloy could possess high yield strength up to 1262 MPa with an excellent 32 5% elongation With almost equivalent ductility. the yield strength obtained was about 16% higher than that of the FeMnAlC (C <= 1 3%) alloys after solution heat-treatment or controlled-rolling followed by an optimal aging at 823 K Additionally, due to the pre-existing fine (Fe,Mn)(3)AlC carbides within the gamma matrix in the as-quenched alloy, the aging time required for attaining the optimal combination of strength and ductility was much less than that of the FeMnAlC (C <= 1 3%) alloys aged at 823 K When the present alloy was aged at 823 K for a time period longer than 4 h. both the strength and ductility were drastically dropped due to the occurrence of gamma(0)/kappa (gamma(0) carbon-deficient austenite) lamellar structure on the gamma/gamma gram boundaries [doi 10.2320/matertrans.M2010013]
URI: http://dx.doi.org/10.2320/matertrans.M2010013
http://hdl.handle.net/11536/5306
ISSN: 1345-9678
DOI: 10.2320/matertrans.M2010013
期刊: MATERIALS TRANSACTIONS
Volume: 51
Issue: 6
起始頁: 1084
結束頁: 1088
顯示於類別:期刊論文


文件中的檔案:

  1. 000280427500006.pdf