標題: High temperature synthesis of Sn-3.5Ag-0.5Zn alloy nanoparticles by chemical reduction method
作者: Lin, C. Y.
Mohanty, U. S.
Chou, J. H.
應用化學系
Department of Applied Chemistry
關鍵字: Chemical reduction;Pb free solder nanoparticle;Sn-3 5Ag-0 5Zn alloy
公開日期: 9-七月-2010
摘要: The synthesis of Sn-3.5Ag-0 5Zn alloy nanoparticles was carried out respectively at 50 and 70 degrees C by using chemical reduction method to examine the temperature effect The stirring times were 3, 12 and 24 h for each temperature X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to investigate the microstructures of the nanoparticle alloys. Xray diffraction patterns revealed that the compound of Ag(3)Sn was formed in the alloying process. Other intermetallic compounds such as Ag(4)Sn and Ag(5)Zn(8) were also obtained in the XRD patterns. Results on TEM revealed that the isolated particles were spherical in shape and the particle size varied from 10 to 20 nm, showing the crystalline nature of the alloy. The nanoparticles obtained were evenly dispersed and less aggregated for the stirring time of 12 h and temperature of 50 degrees C. On the other hand, the nanoparticles obtained at 70 degrees C under the stirring time of 3 h were amorphous in nature and agglomerated which are reflected in the TEM micrographs (C) 2010 Elsevier B.V All rights reserved
URI: http://dx.doi.org/10.1016/j.jallcom.2010.04.111
http://hdl.handle.net/11536/5142
ISSN: 0925-8388
DOI: 10.1016/j.jallcom.2010.04.111
期刊: JOURNAL OF ALLOYS AND COMPOUNDS
Volume: 501
Issue: 2
起始頁: 204
結束頁: 210
顯示於類別:期刊論文