|標題:||BaMgAl10O17 : Eu blue phosphors with MgO coating and microwave irradiation|
Department of Materials Science and Engineering
|摘要:||Europium-activated barium magnesium aluminate (BaMgAl10O17:Eu (BAM)) phosphor particles were modified by surface coating with MgO using a polyol method. The photoluminescence (PL) properties of the MgO-coated BAM phosphors showed slightly improved blue-emission intensity compared to the unmodified ones, and reached a stronger peak intensity with 5.25% MgO coating, under vacuum ultraviolet (VUV) 147 nm excitation. Upon microwave irradiation on the MgO-coated BAM phosphors, the PL properties of the MgO-coated phosphors exhibited a much enhanced relative PL ratio, and a maximum relative PL ratio can be achieved when as high as 10.5% MgO was deposited on the phosphor surface. However, for mechanically ground phosphor powder, it was found that although the intensity of the MgO-coated BAM turned stronger with increasing MgO concentration under microwave irradiation, the purity of the resulting luminescence was slightly disrupted by the presence of a new peak near 470 nm, corresponding to BaMg3Al14O25 compound. (C) 2007 Elsevier Ltd. All rights reserved.|
|期刊:||JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS|
|Appears in Collections:||Conferences Paper|
Files in This Item:
If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.