標題: Poly(phenyl acrylate) and Poly(p-methylphenyl acrylate) as photo-stabilizers II. Protection of PET against photo-oxidation
作者: Lee, CT
Wu, CH
Lin, MS
應用化學系
Department of Applied Chemistry
關鍵字: photo-oxidation;photo-stabilizer;accelerated ageing;functional group changes;retention of tensile strength
公開日期: 1-Mar-2004
摘要: Poly(phenyl acrylate) (PPA) and poly(p-methylphenyl acrylate) (PMPA) were used as inherent photo-stabilizers for PET. PPA/ PET and PMPA/PET in weight ratios of 0/100, 5/95, 10/90, 20/80 and 100/0 were blended. These blends were then cast into films and drawn into fibres and were irradiated with an accelerated weathering tester (QUV). Functional group changes in the films during irradation were monitored with FTIR and the absorbance changes for different samples were compared with one another. Tensile strength of fibres after 42 days of irradiation were tested. Experimental results revealed that when 5% of PPA or PMPA was incorporated into PET, good stabilization of the film and fibres were observed, with PMPA exhibiting more photo-stabilization capability and better retention of tensile strength after 42 days of accelerated aging. (C) 2003 Elsevier Ltd. All rights reserved.
URI: http://dx.doi.org/10.1016/j.polymdegradstab.2003.09.005
http://hdl.handle.net/11536/27004
ISSN: 0141-3910
DOI: 10.1016/j.polymdegradstab.2003.09.005
期刊: POLYMER DEGRADATION AND STABILITY
Volume: 83
Issue: 3
起始頁: 435
結束頁: 440
Appears in Collections:Articles


Files in This Item:

  1. 000189214900010.pdf