標題: White organic light-emitting diodes based on 2,7-bis(2,2-diphenylvinyl)-9,9 '-spirobifluorene: Improvement in operational lifetime
作者: Chuen, CH
Tao, YT
Wu, FI
Shu, CF
應用化學系
Department of Applied Chemistry
公開日期: 15-十一月-2004
摘要: Very bright white organic light-emitting diodes were fabricated using 2,7-bis(2,2-diphenylvinyl)-9,9(')-spirobifluorene (DPVSBF) doped with [4-(dicyanomethylene)-2-t-butyl-6-(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran)] (DCJTB) as the emission layer. With a device configuration of ITO/NPB(40 nm)/DPVSBF:0.2%DCJTB(11 nm)/Alq(30 nm)/LiF(1 nm)/Al(150 nm), a brightness of 1575 cd/m(2) with an external quantum efficiency of 3.31% and luminous efficiency of 8.00 cd/A, a power efficiency of 5.35 lm/W was achieved at a driving current of 20 mA/cm(2) (4.7 V). The brightness reached 66 000 cd/m(2) at 15 V. The Commission Internationale de l'Eclairage coordinates stayed nearly constant, changed from (0.35, 0.36) to (0.32, 0.34) when the voltage increased from 6 to 12 V. The relative operational lifetime of the device increased by a factor of similar to20 compared with a similar device based on 4,4(')-bis-(2,2-diphenylvinyl)-1,1(')-biphenyl as the source of the blue emission. The much extended half-lifetime was attributed to the higher morphological stability of the DPVSBF. (C) 2004 American Institute of Physics.
URI: http://dx.doi.org/10.1063/1.1824178
http://hdl.handle.net/11536/25637
ISSN: 0003-6951
DOI: 10.1063/1.1824178
期刊: APPLIED PHYSICS LETTERS
Volume: 85
Issue: 20
起始頁: 4609
結束頁: 4611
顯示於類別:期刊論文


文件中的檔案:

  1. 000225166400017.pdf