標題: The effect of organo-functional silanes on the adhesion of epoxide resins to ITO glass
作者: Chiang, TH
Hsieh, TE
材料科學與工程學系
Department of Materials Science and Engineering
關鍵字: adhesion strength;ITO glass;silane functional group;epoxide resins
公開日期: 2005
摘要: In this study we investigated five different types of organo-functional silanes containing vinyl, epoxy, amino, methacrylic and acrylic groups in the cationic polymerization of epoxide resin and studied their effects on epoxide adhesion strength to indium tin oxide (ITO) substrate via a pull test. The adhesion strength of epoxide resins was found to be in the order vinyl > methacrylic > acrylic > epoxy > amino. The silane containing vinyl group enhanced the adhesion strength, since it was able to promote free-radical polymerization. As to the silane containing amino group, it retarded the photo-polymerization of cationic photoinitiator in the resin and thus the lowest adhesion strength was observed. It was found that the resin sample containing 1 wt% of vinyl group silane possessed the highest adhesion strength of 91.42 kg/cm(2) to ITO glass. An excessive amount of silane added in the resin generated too much H2O that diluted the concentration of resin and deteriorated the adhesion strength.
URI: http://hdl.handle.net/11536/25423
http://dx.doi.org/10.1163/1568561053066927
ISSN: 0169-4243
DOI: 10.1163/1568561053066927
期刊: JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY
Volume: 19
Issue: 1
起始頁: 1
結束頁: 18