標題: The effect of In2O3 conductive coating on the luminescence and zeta potential of ZnS : Cu, Al phosphors
作者: Chang, CH
Chiou, BS
Chen, KS
Ho, CC
Ho, JC
電子工程學系及電子研究所
Department of Electronics Engineering and Institute of Electronics
關鍵字: phosphors;display;ZnS;surface modification
公開日期: 2005
摘要: Phosphors used in CRTs have been coated with In2O3 conductive layer derived from the hydrolysis of indium chloride. It was found that brightness of the phosphors rises initially with the amount of InCl3, reaches a maximum at 10 Wt-% InCl3 and then decreases when more InCl3 was added. With 10 wt.% InCl3 coating, the brightness of ZnS:Cu, Al phosphor increases by 24% at 800 V and I RA while very little changes were observed in the luminescent emission peak and CIE color loci. The luminescence decay times increase with the increase of the conductive coating. However, they are shorter than 0.7 mu s for samples with the amount of coating ranging from 0 to 20 wt.% InCl3 and are Suitable for display applications. Conductive coating affects the surface chemistry of the phosphor particles, enhances the zeta potential of ZnS:Cu, Al in IPA solution. and, consequently, increases the electrophoretic deposition rate of the phosphors onto substrate. The zeta potential of 10 wt.% InCl3 coated ZnS:Cu, Al in isopropyl alcohol solution is 32 mV as compared to 1.2 mV of that of the uncoated ZnS:Cu, Al. Besides, the electrophoretic deposition rate of the 10 wt.% InCl3 coated ZnS:Cu, Al (0.23 mg/s) is larger than that of the uncoated phosphor (0.17 mg/s). (c) 2005 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
URI: http://hdl.handle.net/11536/25132
http://dx.doi.org/10.1016/j.ceramint.2004.04.011
ISSN: 0272-8842
DOI: 10.1016/j.ceramint.2004.04.011
期刊: CERAMICS INTERNATIONAL
Volume: 31
Issue: 5
起始頁: 635
結束頁: 640
Appears in Collections:Articles


Files in This Item:

  1. 000229358700001.pdf