標題: Structure and properties of gas-nitrided nanostructured FeAlMnC alloy
作者: Chen, Po-Chih
Chao, Chuen-Guang
Juang, Jenh-Yih
Liu, Tzeng-Feng
材料科學與工程學系
電子物理學系
Department of Materials Science and Engineering
Department of Electrophysics
關鍵字: Alloys;Nanostructures;Nitrides;Interfaces
公開日期: 16-十二月-2013
摘要: The as-quenched Fe-9Al-28Mn-1.8C (in wt.%) alloy was directly gas-nitrided at 500 degrees C for 8 h, resulting in a similar to 30 mu m-thick nitrided layer. The nitrided layer consists predominantly of nano-crystalline AlN with a small amount of Fe4N. The nitrogen concentration at surface was extremely high up to similar to 17 wt.% (similar to 41 at.%). Consequently, the surface microhardness (1700 Hv), substrate hardness (550 Hv), ductility (33.2%) and corrosion resistance in 3.5% NaCl solution of the present gas-nitrided alloy are far superior to those obtained previously for the optimally gas-nitrided or plasma-nitrided high-strength alloy steels, as well as martensitic and precipitation-hardening stainless steels. Moreover, it is very novel that the nitrided layer almost remained coherent and adhered well with the matrix after tensile test. Additionally, the present gas nitriding appeared to overcome the edge effects commonly encountered in plasma nitriding treatments for metals. Crown Copyright (C) 2013 Published by Elsevier B.V. All rights reserved.
URI: http://dx.doi.org/10.1016/j.matchemphys.2013.08.063
http://hdl.handle.net/11536/23203
ISSN: 0254-0584
DOI: 10.1016/j.matchemphys.2013.08.063
期刊: MATERIALS CHEMISTRY AND PHYSICS
Volume: 143
Issue: 1
起始頁: 271
結束頁: 274
顯示於類別:期刊論文