標題: Efficient bilayer polymer solar cells possessing planar mixed-heterojunction structures
作者: Huang, Jen-Hsien
Li, Kuang-Chieh
Kekuda, Dhananjay
Padhy, Hari Hara
Lin, Hong-Cheu
Ho, Kuo-Chuan
Chu, Chih-Wei
材料科學與工程學系
光電工程學系
Department of Materials Science and Engineering
Department of Photonics
公開日期: 2010
摘要: We have investigated the influence of thermal annealing on the performance of polymer bilayer solar cell devices incorporating poly{2,6-(4,4-bis[2-ethylhexyl]-4H-cyclopenta[2,1-b;3,4-b'] dithiophene)-alt-4,7-(2,1,3-benzothiadiazole)} (PCPDTTBT) as the donor and two kinds of fullerenes (C(60), C(70)) as acceptors. The higher absorption of C(70) increased the external quantum efficiency in the spectral range 400-600 nm. We observed morphological changes of the polymer films when the pre-annealing temperature was near the crystalline temperature (T(c), 207 degrees C). These nanostructural transformations resulted in a modified interfacial morphology of the donor phases and, therefore, greatly influenced the device performance. Post-annealing treatment reorganized the interface between the donor and acceptor phases, leading to better contact. The highest power conversion efficiency (2.85%) was obtained when we performed device pre- and post-annealing both at 200 degrees C for 30 min; the open-circuit voltage was 0.69 V and the short-circuit current was 8.42 mA cm(-2).
URI: http://hdl.handle.net/11536/20178
http://dx.doi.org/10.1039/b924147g
ISSN: 0959-9428
DOI: 10.1039/b924147g
期刊: JOURNAL OF MATERIALS CHEMISTRY
Volume: 20
Issue: 16
起始頁: 3295
結束頁: 3300