標題: FRACTURE-TOUGHNESS OF ACRYLONITRILE-BUTADIENE-STYRENE BY J-INTEGRAL METHODS
作者: LU, ML
LEE, CB
CHANG, FC
應用化學系
Department of Applied Chemistry
公開日期: 1-九月-1995
摘要: The fracture toughness of acrylonitrile-butadiene-styrene (ABS) was determined by three J-integral methods, ASTM E813-81, E813-87, and by hysteresis. The critical J values (J(1c)) obtained are fairly independent of the specimen thickness, ranging from 10 to 15 mm. ASTM E813-81 and hysteresis methods result in comparable J(1c) values, whereas the ASTM E813-87 was similar to 40% to 50% higher. The critical displacement determined from the plots of hysteresis (energy or ratio) and the true crack grow length vs. displacement are close. This indicates the critical displacement determined by the hysteresis method is indeed the displacement at onset of crack initiation, and the corresponding J(1c) represents a physical event of crack initiation. The elastic storage energy, the input energy minus the hysteresis energy, is the most important factor in determining the onset of crack initiation. The critical elastic storage energy (at the beginning of crack growth) was found close to the J(1c) obtained from the E813-81 or the hysteresis method.
URI: http://hdl.handle.net/11536/1742
ISSN: 0032-3888
期刊: POLYMER ENGINEERING AND SCIENCE
Volume: 35
Issue: 18
起始頁: 1433
結束頁: 1439
顯示於類別:期刊論文


文件中的檔案:

  1. A1995RX60000002.pdf