標題: Phase transitions in an Fe-9Al-30Mn-2.0C alloy
作者: Wang, C. S.
Hwang, C. N.
Chao, C. G.
Liu, T. F.
交大名義發表
National Chiao Tung University
關鍵字: TEM;carbides;spinodal decomposition;Fe-Al-Mn-C alloy
公開日期: 1-Nov-2007
摘要: The as-quenched microstructure of Fe-9Al-30Mn-2.0C alloy is austenite phase containing fine (Fe,Mn)(3)AlC carbides. When the alloy was aged at 900-1100 degrees C and then quenched, both large and extremely fine (Fe,Mn)(3)AlC carbides could be observed simultaneously within the austenite matrix. This feature has never before been observed in FeAlMnC alloy systems. In addition, the Al and Mn concentrations in the coarse (Fe,Mn)(3)AlC carbides formed on the grain boundaries were found to vary drastically with the aging temperature. (C) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
URI: http://dx.doi.org/10.1016/j.scriptamat.2007.07.007
http://hdl.handle.net/11536/10136
ISSN: 1359-6462
DOI: 10.1016/j.scriptamat.2007.07.007
期刊: SCRIPTA MATERIALIA
Volume: 57
Issue: 9
起始頁: 809
結束頁: 812
Appears in Collections:Articles